Preferencje help
Widoczny [Schowaj] Abstrakt
Liczba wyników

Znaleziono wyników: 5

Liczba wyników na stronie
Pierwsza strona wyników Pięć stron wyników wstecz Poprzednia strona wyników Strona / 1 Następna strona wyników Pięć stron wyników wprzód Ostatnia strona wyników

Wyniki wyszukiwania

Wyszukiwano:
w słowach kluczowych:  porous structure
help Sortuj według:

help Ogranicz wyniki do:
Pierwsza strona wyników Pięć stron wyników wstecz Poprzednia strona wyników Strona / 1 Następna strona wyników Pięć stron wyników wprzód Ostatnia strona wyników
Chemical and elemental composition of selected lignocellulose materials was determined and next the materials were used to produce a series of active carbons for electrochemical hydrogen adsorption under strictly repeatable conditions. Chemical activation (900oC) with the application of KOH (4:1) was used for the development of the porous structure. Prior to activation all materials were pyrolysed at 700oC applying a slight temperature increase rate (3oC/min). Produced active carbons had diverse parameters of the porous structure and considerable BET surface areas ranging from 2178 to 2815 m2/g. Experiments showed feasibility of electrosorption of hydrogen on the surface of active carbons produced from commonly available, cheap and frequently waste lignocellulose materials. The type of the applied precursor has a significant effect on the development of the porous structure and hydrogen sorption. The highest hydrogen sorption value of Hc=1.91% weight and Hc=1.90% weight were obtained on AC from cherry stone shells and from oak wood.
Chemical composition of lignocellulose materials and porous structure of activated carbons. Chemical and elemental compositions of selected lignocellulose materials were determined and next a series of activated carbons was produced from these materials under strictly repeatable conditions. The chemical activation method (900oC) using KOH (4:1) was applied for the development of the porous structure. Prior to activation all raw materials were subjected to pyrolysis at 700oC using a slight temperature increase rate (3oC/min). Produced activated carbons had varied porous structure parameters and considerable BET surface areas ranging from 2026 to 2884 m2/g. It was shown that the type of the applied precursor has a significant effect on the development of the porous structure.