Surface roughness after sanding of thermally modified oak wood

• Autorzy: Wilkowski J. , Grzeskiewicz M. , Czarniak P. , Kleczkowski P.

Warianty tytułu

PL

Chropowatość powierzchni po szlifowaniu termicznie modyfikowanego drewna dębu

• Języki publikacji: EN

Abstrakty

EN

Surface roughness after sanding of thermally modified oak wood. In this work influence of thermal oak wood modification on quality surface after sanding with machine CNC equipped with loaf grinding bit was examined. Assesment of surface roughness parameters was realized by mean of contact profilometer. Results show that thermall modification is beneficial to surface quality after sanding. Lower values of roughness parameters were obtained for modified wood.

PL

Chropowatość powierzchni po szlifowaniu termicznie modyfikowanego drewna dębu. W pracy przeanalizowano wpływ procesu termicznej modyfikacji drewna dębu na jakość obrobionej powierzchni po szlifowaniu. Szlifowano na obrabiarce CNC ściernicami listkowymi. Oceny chropowatości powierzchni dokonywano przy pomocy profilometru stykowego. Wyniki wskazują, że modyfikacja termiczna drewna wpływa korzystnie na jakość powierzchni po szlifowaniu. Uzyskiwano niższe wartości parametrów chropowatości powierzchni drewna dębu modyfikowanego.

• Wydawca: -
• Czasopismo: Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology
• Rocznik: 2011
• Tom: 76
• Opis fizyczny: p.208-211,fig.,ref.

Twórcy

autor

Wilkowski J.

• Wood Mechanical Processing Department, Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, ul.Nowoursynowska 159, 02-776 Warsaw, Poland

autor

Grzeskiewicz M.

• Department of Construction and Technology of Final Wood Products, Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, ul.Nowoursynowska 159, 02-776 Warsaw, Poland

autor

Czarniak P.

• Wood Mechanical Processing Department, Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, ul.Nowoursynowska 159, 02-776 Warsaw, Poland

autor

Kleczkowski P.

• Wood Mechanical Processing Department, Faculty of Wood Technology, Warsaw University of Life Sciences-SGGW, ul.Nowoursynowska 159, 02-776 Warsaw, Poland

Bibliografia

• 1. HILL C., 2006: Wood Modification: Chemical, Thermal and Other Processes. John Wiley & Sons, Ltd., 99-130.
• 2. GRZEŚKIEWICZ M., KRAWIECKI J., 2008: Thermally modified ash and oak wood as materials for parquets – mechanical properties of the wood and its resistance for different kinds of wood finishing. Annals of Warsaw University of Life Sciences- SGGW Forestry and Wood Technology No 65: 93-97.
• 3. WIELOCH G., ADAMSKI Z., MOSTOWSKI R., 2009: The interaction of abrasive grains on the thermally modified surface of acacia wood during grinding. Annals of Warsaw University of Life Sciences – Forestry and Wood Technology 69, s.409-414.
• 4. WILKOWSKI J., GRZEŚKIEWICZ M., CZARNIAK P., LITWA M., 2010: Influence of wood thermal modification on cutting resistance during drilling. Annals of Warsaw University of Life Sciences- SGGW Forestry and Wood Technology No 72: 480-48.