On organic coatings in marine applications

• Autorzy: Darowicki K , Szocinski M.
• Języki publikacji: EN

Abstrakty

EN

A number of marine structures fail due to the fatigue damage resulting from cyclic mechanical stress. However, as far as coatings are concerned this degradation factor remains underestimated. In the paper the authors propose the methodology for the evaluation of coating resistance to an impact of repetitive mechanical stress. Typical epoxy coating designated for ship hull protection has been tested in as-received state as well as after pre-exposure to UV radiation and elevated temperature.

Słowa kluczowe

EN

sea surface safety; marine application; sea subsurface safety; vessel; cyclic mechanical stress; marine conference; fatique damage; conference; Polish Navy; organic coating

• Wydawca: -
• Czasopismo: Polish Journal of Environmental Studies
• Rocznik: 2005
• Tom: 14
• Numer: Suppl.1
• Opis fizyczny: p.166-170,fig.,ref.

Twórcy

autor

Darowicki K

• Gdansk University of Technology, G.Narutowicza Str.11/12, 80-952 Gdansk, Poland

autor

Szocinski M.

Bibliografia

• 1. Paint and Surface Coatings: Theory and Practice, editor R. Lambourne, John Wiley & Sons: New York, pp 533- 543, 1987.
• 2. KOTNAROWSKA D.: Influence of ultraviolet radiation and aggressive media on epoxy coating degradation. Prog. Org. Coat. 37, 149, 1999.
• 3. MISZCZYK A., DAROWICKI K.: Effect of environmental temperature variations on protective properties of organic coatings. Prog. Org. Coat. 46, 49, 2003.
• 4. MISZCZYK A., DAROWICKI K. Accelerated ageing of organic coating systems by thermal treatment. Corros. Sci. 43, 1337, 2001.
• 5. HOLZHAUSEN U., MILLOW S., ADLER H. J. P.: Studies on the thermal ageing of organic coatings. Macromol. Symp. 187, 939, 2002.
• 6. MISZCZYK A., DAROWICKI K., SCHAUER TH.: Evaluation of relative humidity effects on interfacial impedance at inter-coat interfaces. Pol. J. Chem. 78, 1823, 2004.
• 7. ROBLES L. B. R., BUELTA M. A., GONCALVES E., SOUZA G. F. M.: A method for the evaluation of the fatigue operational life of submarine pressure hulls. Int. J. Fatigue 22, 41, 2000.
• 8. DAROWICKI K., SZOCIŃSKI M.: Evaluating the performance of organic coatings under mechanical stress using electrochemical impedance spectroscopy. J. Solid State Electrochem. 346 (8), 346, 2004.
• 9. BIELAJEW M. M.: Materials durability, Published by Ministry of Defense: pp 339- 345, 1956 (in Polish).
• 10. BOUKAMP B. A.: Equivalent Circuit (Equivcrt. pas) - Users manual, University of Twente: The Netherlands, 1988.