Effect of the press closing speed on mechanical properties of particleboards with the core layer made from willow (Salix viminalis)

• Autorzy: Warmbier K. , Wilczynski A. , Danecki L. , Mrozek M.

Warianty tytułu

PL

Wpływ prędkości zamykania prasy na właściwości mechaniczne płyt wiórowych z warstwą wewnętrzną wykonaną z wierzby Salix viminalis

• Języki publikacji: EN

Abstrakty

EN

Effect of the press closing speed on mechanical properties of particleboards with the core layer made from willow (Salix viminalis). Three-layer experimental particleboards were prepared using basket willow (Salix viminalis) particles for the core layer and industrial pine particles for the face layers. The effect of the speed of press closing (1, 2 and 3 mm/s from the mat thickness to the distance bar) on modulus of elasticity (MOE), modulus of rupture (MOR) and internal bond (IB) was investigated. The greater speed provided better MOE and MOR, and worse IB. For comparison, the properties of particleboards with the core layer made from pine particles were studied. MOE and MOR of particleboards with the core layer from willow were slightly smaller, and IB was slightly greater.

PL

Wpływ prędkości zamykania prasy na właściwości mechaniczne płyt wiórowych z warstwą wewnętrzną wykonaną z wierzby Salix viminalis. Wykonano trzywarstwowe płyty wiórowe stosując wióry wierzby wiciowej (Salix viminalis) na warstwę wewnętrzną i przemysłowe wióry sosnowe na warstwy zewnętrzne. Badano wpływ prędkości zamykania półek prasy (1, 2 i 3 mm/s - od grubości maty do trzpienia dystansowego) na moduł sprężystości (MOE), wytrzymałość na zginanie (MOR) i wytrzymałość na rozciąganie poprzeczne (IB). Większa prędkość zapewniała lepsze MOE i MOR oraz gorsze IB. Dla porównania badano właściwości płyt z warstwą wewnętrzną wykonaną z wiórów sosnowych. MOE i MOR płyt wiórowych z warstwą wewnętrzną z wiórów wierzbowych były nieznacznie mniejsze, a IB nieznacznie większe.

• Wydawca: -
• Czasopismo: Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology
• Rocznik: 2011
• Tom: 76
• Opis fizyczny: p.168-171,fig.,ref.

Twórcy

autor

Warmbier K.

• Institute of Technology, Kazimierz Wielki University, Chodkiewicza 30 str., 85-064 Bydgoszcz, Poland

autor

Wilczynski A.

• Institute of Technology, Kazimierz Wielki University, Chodkiewicza 30 str., 85-064 Bydgoszcz, Poland

autor

Danecki L.

• Research and Development Centre for Wood-Based Panels Industry in Czarna Woda, Mickiewicza 10 str., 83-262 Czarna Woda, Poland

autor

Mrozek M.

• Research and Development Centre for Wood-Based Panels Industry in Czarna Woda, Mickiewicza 10 str., 83-262 Czarna Woda, Poland

Bibliografia

• 1. DUBAS J., TOMCZYK A. (2005) Establishment, care and protection of energetic willow plantation (in Polish). SGGW Warszawa.
• 2. EN 310 (1993) Wood-based panels. Determination of modulus of elasticity in bending and of bending strength.
• 3. EN 312 (2003) Particleboards. Specifications.
• 4. EN 319 (1993) Particleboards and fiberboards. Determination of tensile strength perpendicular to the plane of the board.
• 5. FRĄCKOWIAK I., 2007: From studies on using alternative lignocellulosic raw materials for particleboard production (in Polish). Technologia Drewna - Wczoraj, Dziś, Jutro, Poznań: 285-294.
• 6. FRĄCKOWIAK I., FUCZEK D., KOWALUK G., 2008: Impact of different lignocellulosic materials used in core of particleboard on modulus of elasticity and bending strength. DREWNO-WOOD 51, 180: 5-13.
• 7. SEAN S.T., LABRECQUE M. (2006) Use of short-rotation coppice willow clones of Salix viminalis as furnish in panel production. Forest Products Journal 56 (9): 47-52.
• 8. SZCZUKOWSKI S., TWORKOWSKI J., STOLARSKI M. (2006) Energetic willow (in Polish). Plantpress, Kraków.
• 9. WARMBIER K., WILCZYŃSKI A., DANECKI L. (2010) Particle size dependent properties particleboards with the core layer made from willow (Salix viminalis). Annals of Warsaw University of Life Sciences. Forestry and Wood Technology 71: 405-409.
• 10. WILCZYŃSKI A., WARMBIER K., DANECKI L., MROZEK M. (2011) Properties of experimental particleboards with the core layer made from willow (Salix viminalis). Annals of Warsaw University of Life Sciences. Forestry and Wood Technology 74.