Insulation boards from thermoplastic bonded bark

• Autorzy: Borysiuk P. , Derda M. , Jenczyk-Tolloczko I.

Warianty tytułu

PL

Płyty izolacyjne z kory spajanej termoplastem

• Języki publikacji: EN

Abstrakty

EN

Insulation boards from thermoplastic bonded bark. Within this work, boards from thermoplastic bonded bark were made. Grinded bark of coniferous species and recycled polyethylene were used. Four variants of boards were manufactured: three of varying polyethylene weight ratio: 30, 40 and 50%, and fourth UF resin bonded. Assumed density of boards was 300 kg/m3, and thickness of 18 mm. Manufactured boards were examined for density, thermal properties, MOR, and swelling. Research has shown that production of insulation boards from PE bonded bark is possible. With the increase in thermoplastic weight ratio, thermal insulation of boards decreases, and their mechanical properties increases.

PL

Płyty izolacyjne z kory spajanej termoplastem. W ramach pracy wykonano płyty z kory spajane termoplastem. Wykorzystano rozdrobnioną korę drzew gatunków iglastych oraz pochodzący z recyklingu polietylen. Wytworzono cztery warianty płyt: trzy o różnym udziale wagowym polietylenu: 30, 40 i 50%, oraz czwartą spajaną żywicą UF. Założona gęstość płyt wynosiła 300 kg/m3, a grubość 18 mm. Dla wytworzonych płyt zbadano gęstość, właściwości cieplne, MOR, spęcznienie. Badania wykazały, że istnieje możliwość wytworzenia płyt termoizolacyjnych z kory spajanej PE. Wraz ze wzrostem udziału wagowego termoplastu spada termoizolacyjność płyt, zaś wzrastają ich właściwości mechaniczne.

Słowa kluczowe

EN

insulation board; thermo-insulating board; bark; thermoplastic material; polyethylene; urea-formaldehyde resin; thermal insulation; thermal property; rupture modulus; swelling property; density; thickness; mechanical property

• Wydawca: -
• Czasopismo: Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology
• Rocznik: 2012
• Tom: 77
• Opis fizyczny: p.86-89,ref.

Twórcy

autor

Borysiuk P.

• Faculty of Wood Technology, Warsaw University of Life Sciences -SGGW, 159 Nowoursynowska St., 02-776 Warsaw, Poland

autor

Derda M.

• Faculty of Wood Technology, Warsaw University of Life Sciences -SGGW, 159 Nowoursynowska St., 02-776 Warsaw, Poland

autor

Jenczyk-Tolloczko I.

• Faculty of Wood Technology, Warsaw University of Life Sciences -SGGW, 159 Nowoursynowska St., 02-776 Warsaw, Poland

Bibliografia

• 1. ANTKOWIAK L., 1997: Wykorzystanie kory niektórych drzew i krzewów. Wydawnictwo Akademii Rolniczej w Poznaniu.
• 2. BLANCHET P., CLOUTIER A., RIEDL B., 2000: Particleboard made from hammer milled black spruce bark residues. Wood Science and Technology 34, 11-19.
• 3. BORYSIUK P., MAMIŃSKI M., ZADO A., 2009: Some comments on the manufacturing of thermoplastic-bonded particleboards. Annals of Warsaw University of Life Sciences – SGGW, Forestry and Wood Technology No 68/09, 50-54.
• 4. EN 310 Wood-based panels. Determination of modulus of elasticity in bending and of bending strength
• 5. EN 317 Particleboards and fibreboards. Determination of swelling in thickness after immersion in water
• 6. EN 319 Particleboards and fibreboards. Determination of tensile strength perpendicular to the plane of the board
• 7. EN 622-4 Fibreboards. Specifications. Requirements for softboards
• 8. EN ISO 6946 Building components and building elements. Thermal resistance and thermal transmittance. Calculation method
• 9. GOZDECKI C., KOCISZEWSKI M., MIROWSKI J., WILCZYŃSKI A., ZAJCHOWSKI S., 2009: Effect of wood bark on wood-plastic composite properties. Annals of Warsaw University of Life Sciences, Forestry and Wood Technology, 68, 278-282
• 10. GOZDECKI C., KOCISZEWSKI M., WILCZYŃSKI A., MIROWSKI J., 2010: Effect of wood bark content on mechanical properties of wood-polyethylene composite. Annals of Warsaw University of Life Sciences, Forestry and Wood Technology, 71, 203-206
• 11. MUSZYŃSKI Z., McNATT J.D., 1984: Investigations on the use of spruce bark in the manufacture of particleboard in Poland. Forest Prod. J. 34(1), 28-35.