The effect of pressing time on properties of particleboards resinated with phenoi-formaldehyde resin modified with polyols

• Autorzy: Mirski R. , Dziurka D. , Lecka J.

Warianty tytułu

PL

Wpływ czasu prasowania na właściwości płyt wiórowych zaklejanych żywicą fenolowo-formaldehydową modyfikowaną alkoholami wielowodorotlenowymi

• Języki publikacji: EN

Abstrakty

EN

The effect of pressing time on properties of particleboards resinated with phenol-formaldehyde resin modified with polyols. The study investigated the effect of modification of phenolic resin with polyols such as ethylene glycol, propylene glycol, butylene glycol and glycerol on the possibility to shorten pressing time for particleboards manufactured with the use of such modified PF resin. Tests showed that all types of polyols added to resin considerably improved physico-mechanical properties of manufactured boards. The application of butylene glycol or glycerol makes it possible to manufacture boards with good properties at pressing time shortened by 20%.

PL

W pracy zbadano wpływ modyfikacji żywicy fenolowej alkoholami wielowodorotlenowymi, takimi jak: 1,2-etandiol, 1,3-propandiol, 1,4-butandiol, 1,2,3-propantriol, na możliwość skrócenia czasu prasowania płyt wiórowych, wytwarzanych przy użyciu tak zmodyfikowanej żywicy PF. Badania wykazały, iż wszystkie rodzaje dodawanych do żywicy alkoholi wielowodorotlenowych znacznie poprawiają fizko-mechaniczne właściwości wytworzonych płyt. Zastosowanie natomiast jako modyfikatora 1,4 - butandiolu lub 1,2,3 - propantriolu, pozwala na wytworzenie płyt o dobrych właściwościach w skróconym o 20% czasie prasowania.

• Wydawca: -
• Czasopismo: Annals of Warsaw Agricultural University. Forestry and Wood Technology
• Rocznik: 2005
• Tom: 57
• Opis fizyczny: p.55-59,ref.

Twórcy

autor

Mirski R.

• Department of Wood-Based Materials, August Cieszkowski Agricultural University of Poznan, Wojska Polskiego 38/42, 60-627 Poznan, Poland

autor

Dziurka D.

autor

Lecka J.

Bibliografia

• 1. HAUPT R. A., SELLERS Т., 1994; Charakterizations of phenol-formaldehyde resol resins, American Chemical Society; 693-697.
• 2. WANG X.M., RIEDL В., CHRISTIANSEN A.W., GEIMER R.L., 1995; The effects of temperature and humidity on phenol-formaldehyde resin bonding. Wood Sci. Technol. 29; 253-266.
• 3. CHUANG I.S., MACIEL G.E., 1991; 13C NMR investigation of the stability of a reasol - type phenol-formaldehyde resin toward formalin, toward base, and toward nonoxidizing or oxidizing acid, Macromolecules 24(5); 1025-1032.
• 4. JELLINEK K., MÜLLER R., 1982; Fortschritte auf dem Gebiet der Phenolharz- Spanplatte V 100, Holz-Zentralblatt 52. Przekład artykułu zamieszczony w Przemyśle Drzewnym nr 10; 9-10.
• 5. ANDERSEN A.W., TROUGHTON G.E., 1996; New phenolic formulations for bonding higher moisture content OSB panels, For. Prod. J. 46(10); 72-76.
• 6. IRLE M.A., BOLTON A.J., 1988; Physical Aspects of Wood Adhesive Bond Formation with Formnaldehyde Based Adhesives. Part II. Binder Physical Properties and Particleboard Durability, Holzforschung 42(1); 53-58.
• 7. FIDELUS A., 1983; Szybko utwardzalne kompozycje z żywic fenolowo- formaldehydowych, Przem. Drzew, nr 9; 11-14.
• 8. ELBERT A.A., 1984; Chimiczeskaja technologia drevesnostružecznych plit, Lesnaja Promyszlennost, Moskwa.
• 9. PIZZI A., STEPHANOU A., 1994; Phenol-formaldehyde wood adhesives under very alkaline conditions. Part II: Esters curing acceleration, its mechanism and applied results, Holzforschung 48(2); 150-156.
• 10. TOHMURA S., HIGUCHI M. 1995; Acceleration of the cure of phenolic resin adhesives VI. Cure accelerating action of propylene carbonate, J. Jap. Wood Res. Soc.41(12); 1109-1114.
• 11. ŁĘCKA J., MIRSKI R., DZIURKA D. 2001; The effect of polyalcohols on the properties of paricleboards glued with phenolic-formaldehyde resin, Zeszyty Naukowe Politechniki Śląskiej, Chemia z. 146; 181-185.

Uwagi

PL

Rekord w opracowaniu