Formaldehyde content in and VOC release from particleboards made of fibrous chips

• Autorzy: Kowaluk G. , Komorowicz M. , Witczak M. , Fuczek D.

Warianty tytułu

PL

Zawartość formaldehydu i emisja VOC płyt wiórowych wytworzonych z wiórów włóknistych

• Języki publikacji: EN

Abstrakty

EN

The aim of this research was to investigate formaldehyde content in and volatile organic compounds release from particleboards produced from fibrous chips. The object of the tests were panels produced from fibrous chips of black locust Robinia Pseudoacacia L. and willow Salix Viminalis L., as well as from typical industrial particles. The results show that formaldehyde content in the panels produced from willow fibrous chips is similar to the content in the panels made of industrial particles. The concentration of total volatile organic compounds measured after 4 weeks of storage is significantly lower than the required by the existing regulations.

PL

Celem badań było określenie zawartości formaldehydu w płytach wiórowych wytworzonych z wiórów włóknistych i emisji lotnych związków organicznych z tych płyt. Do badań użyto wiórów włóknistych z dwuletnich odrostów korzeniowych robinii (Robinia Pseudoacacia L.) oraz wierzby (Salix Viminalis L.), jak również typowych wiórów przemysłowych. Badania wykazały, iż zawartość formaldehydu w płytach wytworzonych z wierzby jest zbliżona do zawartości formaldehydu w płytach z wiórów przemysłowych. Stężenie lotnych związków organicznych, mierzone po 4 tygodniach przechowywania płyt, jest istotnie mniejsze niż obowiązujące ograniczenia.

Słowa kluczowe

EN

formaldehyde content; volatile organic compound; particle board; fibrous chip; willow; black locust

• Wydawca: -
• Czasopismo: Drewno. Prace Naukowe. Doniesienia. Komunikaty
• Rocznik: 2011
• Tom: 54
• Numer: 185
• Opis fizyczny: p.81-88,fig.,ref.

Twórcy

autor

Kowaluk G.

• Wood Technology Institute, Poznan, Poland

autor

Komorowicz M.

• Wood Technology Institute, Poznan, Poland

autor

Witczak M.

• Wood Technology Institute, Poznan, Poland

autor

Fuczek D.

• Wood Technology Institute, Poznan, Poland

Bibliografia

• AgBB [2008]: Health-Related Evaluation Procedure for Volatile Organic Compounds Emissions (VOC and SVOC) from Building Products. <http://www.umweltbundesamt.de/produkte-e/bauprodukte/archive/AgBB-Evaluation-Scheme2008.pdf>
• Dünisch O., Richter H.-G., Koch G. [2010]: Wood properties of juvenile and mature heartwood in Robinia pseudoacacia L. Wood Sci. Technol. 2010 [44]:301–313
• Dziewanowska-Pudliszak A., Gaca P. [2004]: How many organic compounds does the furniture emit? Gazeta Drzewna 11[73]: 15, 16 (in polish)
• Kowaluk G. [2009]: Influence of the method of milling on the geometry of fibrous chips and bending strength of produced particleboards. Proc. 3rd Int. Sc. Conf. Woodworking Techniques. Zalesina: 323-331
• Kowaluk G., Zbiec M., Beer P. [2010]: The quality of milling of the particleboards produced from fibrous chips. Ann. WULS-SGGW, For. and Wood Technol. 71
• Roffael E. [2006]: Volatile organic compounds and formaldehyde in nature, wood and wood based panels. Holz als Roh- und Werkstoff [64]: 144–149
• Schäfer M., Roffael E. [2000]: On the formaldehyde release of wood. Holz als Roh- und Werkstoff [58]: 259-264
• Weigl M., Wimmer R., Sykacek E.; Steinwender M. [2009]: Wood-born formaldehyde varying with species, wood grade, and cambial age. Forest Product Journal [59] 1/2: 88-92
• Yrieix Ch., Dulaurent A., Laffargue C., Maupetit F., Pacary T., Uhde E. [2010]: Characterization of VOC and formaldehyde emissions from a wood based panel: Results from an inter-laboratory comparison. Chemosphere [79]: 414–419