Strength properties of structurally reinforced plywood

• Autorzy: Borysiuk P. , Latuszkiewicz Z. , Jenczyk-Tolloczko I.

Warianty tytułu

PL

Właściwości wytrzymałościowe sklejek wzmocnionych strukturalne

• Języki publikacji: EN

Abstrakty

EN

Strength properties of structurally reinforced plywood. The study determined the degree of improvement of mechanical properties of 19 layer beech plywood with a thickness of 10 mm by introducing two layers of structural reinforcement in the form of aramid, glass and carbon fabric. For manufactured plywood, density, static bending strength and modulus of elasticity in static bending, toughness strength and impact bending strength were examined. It was determined, that the use of carbon, aramid and glass fabrics bonded with epoxy glue for structural reinforcement of plywood, has positive effect on strength parameters. The best results of improvement to the strength parameters of plywood is achieved by inserting two layers of carbon fabric.

PL

Właściwości wytrzymałościowe sklejek wzmocnionych strukturalne. W ramach badań określano stopień poprawy właściwości wytrzymałościowych 19 warstwowych sklejek bukowych o grubości 10 mm poprzez wprowadzenie 2 warstw wzmocnienia strukturalnego w postaci tkanin aramidowej, szklanej i węglowej. Dla wytworzonych sklejek oznaczono gęstość, wytrzymałość na zginanie statyczne i moduł sprężystości przy zginaniu statycznym, udarność i wytrzymałość na zginanie dynamiczne. Ustalono, że zastosowanie do strukturalnego wzmocnienia sklejek tkanin: węglowej, aramidowej i szklanej zaklejanych klejem epoksydowym wpływa korzystnie na parametry wytrzymałościowe. Najlepsze efekty poprawy parametrów wytrzymałościowych sklejek zapewnia wprowadzenie 2 warstw tkaniny węglowej.

Słowa kluczowe

EN

composite material; plywood; reinforced plate; reinforcing material; aramid fabric; carbon fabric; glass fabric; epoxy adhesive; strength parameter; material density; dynamic bending strength; elasticity modulus; static bending strength; impact resistance

• Wydawca: -
• Czasopismo: Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology
• Rocznik: 2012
• Tom: 77
• Opis fizyczny: p.90-94,fig.,ref.

Twórcy

autor

Borysiuk P.

• Faculty of Wood Technology, Warsaw University of Life Sciences -SGGW, 159 Nowoursynowska St., 02-776 Warsaw, Poland

autor

Latuszkiewicz Z.

• Faculty of Wood Technology, Warsaw University of Life Sciences -SGGW, 159 Nowoursynowska St., 02-776 Warsaw, Poland

autor

Jenczyk-Tolloczko I.

• Faculty of Wood Technology, Warsaw University of Life Sciences -SGGW, 159 Nowoursynowska St., 02-776 Warsaw, Poland

Bibliografia

• 1. BIBLIS E. J., CARINO H. F., 2000: Flexural properties of Southern pine plywood overlaid with fiberglass reinforced plastic. Forest Products Journal, 50 (4), 34 - 36.
• 2. BORYSIUK P., MAMIŃSKI M., BORUSZEWSKI P., JABŁOŃSKI M., 2008: Studies on the structural reinforcement of plywood with the glass-fiber netting. VIIth International Symposium: „Composite Wood Materials”, Zvolen, June 25-27 2008 r, 100-103
• 3. BRODY H., 1987: Tennis science for tennis players, University of Pennsylvania Press, Pennsylvania
• 4. BROWN R. P., 2001: Polymers in Sport and Leisure, Rapra Reviev Reports, 3, 10-11
• 5. EN 310:1994: Płyty drewnopochodne. Oznaczanie modułu sprężystości przy zginaniu i wytrzymałości na zginanie, PKN, Warszawa
• 6. EN 323:1999: Płyty drewnopochodne. Oznaczanie gęstości, PKN, Warszawa
• 7. GREWAL D., ROSSETTER E., LUND C., EWERS B. J., 2009: Experimental measurement of selected snowboard mechanical properties. The Engineering of Sport, 7(2), 279-287
• 8. LAM F., PRION H. G. L., 2003: Timber engineering, Wiley Editional Office, West Sussex, England
• 9. LEDA H., 2006: Kompozyty polimerowe z włóknami ciągłymi: wytwarzanie, właściwości, stosowanie. Wyd. I, Wydawnictwo Politechniki Poznańskiej, Poznań
• 10. MILEWSKI Z., 1999: Projektowanie i budowa jachtów żaglowych. Wydawnictwo Morskie, Gdańsk.
• 11. MOST B., 1988: Gold medal. Popular mechanics, 3, 74
• 12. PN-D-04104:1979: Drewno. Oznaczanie udarności i wytrzymałości na zginanie dynamiczne, PKN, Warszawa
• 13. STARECKI A., JABŁOŃSKI M. 1998: Selected properties of plywood with fibrous midle layer. II Międzynarodowe Sympozjum. Zvolen 9-10 września 1998r., 281-284
• 14. VAIDYA U. K., JANOWSKI G. M., ANDREWS J. B., DWYER Z., RIGNEY D., 2004: Composite skateboard design and construction experience for freshmen engineering students, American Society for Composites/American Society for Testing And Materials, 29-37
• 15. XU H., TANAKA C, NAKAO T., NISHINO Y., KATAYAMA H., 1996: Flexural and shear properties of fiber-reinforced plywood. Mokuzai Gakkaishi (Journal of the Japan Wood Research Society), 42 (4), s. 376-382.
• 16. YOUNGQUIST J. A., 1995: Unlikely Partners? The marriage of wood and nonwood materials. Forest Products Journal, 45(10), 30