Tytuł artykułu

Effect of some manufacturing parameters on mechanical properties of particleboards with the core layer made from willow Salix viminalis

Treść / Zawartość
Warianty tytułu
PL
Wpływ wybranych parametrów wytwarzania na właściwości mechaniczne płyt wiórowych z warstwą wewnętrzną z wierzby Salix viminalis
Języki publikacji
EN
Abstrakty
EN
Effects of manufacturing parameters on mechanical properties of particleboards with the core layer made from willow Salix viminalis. Three-layer experimental particleboards were prepared using the willow Salix viminalis particles for the core layer and industrial pine particles for the face layers. The press temperature (180 and 200°C), press time (4 and 6 min) and shelling ratio (0.3 and 0.4) were variable parameters. The modulus of elasticity (МОЕ), modulus of rupture (MOR), internal bond (IB) and screw holding strength (SHS) of particleboards were investigated. In general, the considered factors significantly affected the mechanical properties of particleboards.
PL
Wpływ wybranych parametrów wytwarzania na właściwości mechaniczne płyt wiórowych z warstwą wewnętrzną z wierzby Salix viminalis. Wykonano trzywarstwowe płyty wiórowe stosując wióry wierzby Salix viminalis na warstwę wewnętrzną i przemysłowe wióry sosnowe na warstwy zewnętrzne. Parametrami zmiennymi były: temperatura prasowania (180 i 200°C), czas prasowania (4 i 6 min) i stosunek grubości warstw zewnętrznych do grubości płyty (0.3 i 0.4). Badano moduł sprężystości (MOE), wytrzymałość na zginanie (MOR), wytrzymałość na rozciąganie poprzeczne (IB) i zdolność utrzymania wkręta (SHS). Uwzględnione parametry na ogół oddziaływały istotnie na badane właściwości mechaniczne.
Słowa kluczowe
Wydawca
-
Rocznik
Tom
88
Opis fizyczny
p.277-281,fig.,ref.
Twórcy
autor
  • Institute of Technology, Kazimierz Wielki University, Chodkiewicza 30, 85-064 Bydgoszcz, Poland
  • Institute of Technology, Kazimierz Wielki University, Chodkiewicza 30, 85-064 Bydgoszcz, Poland
autor
  • Research and Development Centre for Wood-Based Panels Industry in Czarna Woda, Czarna Woda, Poland
Bibliografia
  • 1. ASHORI A., NOURBAKHSH., 2008: Effect of press cycle time and resin content on physical and mechanical properties of particleboard panels made from the underutilized low-quality materials. Industrial Crops and Products 28: 225-230.
  • 2. AZIZIK., TABARSA T., ASHORI A., 2011: Performance characterizations of particleboards made with wheat straw and waste veneer splinters. Composites: Part B 42: 2085-2089.
  • 3. EN 310, 1993: Wood-based panels. Determination of modulus of elasticity in bending and of bending strength.
  • 4. EN 319, 1993: Particleboards and fiberboards. Determination of tensile strength perpendicular to the piane of the board.
  • 5. EN 13446, 2002: Wood-based panels. Determination of withdrawal capacity of fasteners.
  • 6. FRĄCKOWIAK I., FUCZEK D., KOWALUK G., 2008: Impact of different lignocellulosic materials used in core of particleboard on modulus of elasticity and bending strength. Drewno – Wood 51: 5-13.
  • 7. GHALEHNO M.D., MADHOUSHI M., TABARSA T., NAZERIAN M., 2011: The manufacture of particleboards using mixture of reed (surface layer) and commercial species (middle layer). Eur. J. Wood Prod. 69:341-344.
  • 8. KALAYCIOGLU H., NEMLI G., 2006: Producing composite particleboard from kenaf (Hibiscus cannabinus L.) stalks. Industrial Crops and Products 24: 177-180.
  • 9. KOWALUK G., 2009: Influence of the density on the mechanical properties of the particleboards produced from fibrous chips. Ann. WULS-SGGW, For and Wood Technol 68: 397-400.
  • 10. KOWALUK G., 2011: Influence of particles fraction used for surface layer on particleboard strength. Ann. WULS-SGGW, For and Wood Technol 74: 212-215.
  • 11. KOWALUK G., FUCZEK D., 2010: Screw holding performance of panels made of fibrous chips. Drewno. Pr. Nauk. Donieś. Komunik. 53: 77-81.
  • 12. KOWALUK G., FUCZEK D., BEER P., GRZEŚKIEWICZ M., 2011: Influence of the raw materials and production parameters on the chosen standard properties for furniture panels of biocomposites from fibrous chips. Bioresources 6 (3): 3004-3018.
  • 13. SEAN S.T., LABRECQUE M., 2006: Use of short-rotation coppice willow clones of Salix viminalis as furnish in panel production. Forest Prod J 56 (9): 47-52.
  • 14. TABARSA T., ASHORI A., GHOLAMZADEH M., 2011: Evaluation of surface roughness and mechanical properties of particleboard panels made from bagasse. Composite: Part B 42: 1330-1335.
  • 15. WARMBIER K., WILCZYŃSKI A., DANECKI L., 2010: Particle size dependent particleboards with the core layer made from willow (Salix viminalis). Ann WULS-SGGW, For and Wood Technol 71: 405-409.
  • 16. WARMBIER K., WILCZYŃSKI A., DANECKI L., MROZEK M., 2011: Effect of the press closing time on mechanical properties of particleboards with the core layer made from willow (Salix viminalis). Ann WULS-SGGW, For and Wood Technol 76: 168-171.
  • 17. WARMBIER K., WILCZYŃSKI A., DANECKI L., 2013: Properties of one-layer experimental particleboards from willow (Salix viminalis) and industrial wood particles. Eur J Wood Prod 71: 25-28.
  • 18. WARMBIER K., WILCZYŃSKI A., DANECKI L., 2013: Effects of density and resin content on mechanical properties of particleboards with the core layer made from willow (Salix viminalis). Ann WULS-SGGW, For and Wood Technol 84: 284-287.
  • 19. WARMBIER K., WILCZYŃSKI A., DANECKI L., 2014: Evaluation of mechanical and physical properties of particleboards with the core layer made from willow (Salix viminalis) BioResources 9: 894-905.
  • 20. WILCZYŃSKI A., WARMBIER K., DANECKI L., MROZEK M., 2011: Properties of experimental particleboards with the core layer made from willow (Salix viminalis). Ann WULS-SGGW, For and Wood Technol 76: 194-198.
Typ dokumentu
Bibliografia
Identyfikatory
Identyfikator YADDA
bwmeta1.element.agro-6d28a847-0b61-4ae2-9558-0732af5bedf0
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.