Gluing of polystyrene and methyl polymethacrylate modified wood with melamine-urea resin

• Autorzy: Dziurka D. , Jablonski M. , Zbiec M.

Warianty tytułu

PL

Klejenie żywicą melaminowo-mocznikową drewna zmodyfikowanego polistyrenem oraz poli(metakrylanem metylu)

• Języki publikacji: EN

Abstrakty

EN

Polystyrene and methyl polymethacrylate modified beech and alder wood was glued with melamine-urea resin. Unmodified wood was also glued as a reference. Shear and compression strength of glue joints was tested, in dry state, after 24h damping and 6 hour boiling with 18h cooling. It was stated, that melamine-urea resin is suitable for gluing of polystyrene and methyl polymethacrylate modified wood. Dimensional stability of modified wood increases strength of Dynomel L-435 glue joints. Wood modified with thermally hardened polystyrene in mineral oil requires preparation - removal of outer layer.

PL

Klejono klejem melaminowo- formaldehydowym, drewno bukowe i olchowe zmodyfikowane polistyrenem oraz poli metakrylanem metylu). W celu porównania klejono również drewno naturalne. Badano wytrzymałość spoin klejowych na ścinanie przy ściskaniu na sucho, po 24 godzinnym moczeniu w wodzie zimnej oraz po 6 godzinach gotowania w wodzie i 18 godzinach studzenia. Stwierdzono, ze klej melaminowo-formaldehydowy nadaje się do klejenia drewna zmodyfikowanego polistyrenem i poli metakrylanem metylu). Stabilność wymiarowa drewna zmodyfikowanego wpływa korzystnie na wytrzymałość spoin klejowych przy zastosowaniu kleju Dynomel L-435. Drewno zmodyfikowane polistyrenem utwardzanym termicznie w oleju mineralnym wymaga przygotowania powierzchni poprzez zdjęcie warstwy wierzchniej.

• Wydawca: -
• Czasopismo: Annals of Warsaw Agricultural University. Forestry and Wood Technology
• Rocznik: 2004
• Tom: 55
• Opis fizyczny: p.169-173,fig.,ref.

Twórcy

autor

Dziurka D.

• Department of Wood-Based Materials, Agricultural University of Poznan, Wojska Polskiego str. 38/42, 60-627 Poznan, Poland

autor

Jablonski M.

autor

Zbiec M.

Bibliografia

• 1. DZIURKA D„ŁĘCKA J., 2004: The effect of methods of introducing acrylic emulsions grafted with acetoacetyl groups on the properties of particleboards. J. Appl. Polym. Sei. Vol. 91(4), 2256-2264.
• 2. DZIURKA D., ŁĘCKA J., MIRSKI M, 2003: The effect of grafting particles with acetoacetyl groups on the properties of particleboards. Electronic Journal of Polish Agricultural Universities. Vol. 6. Issue 2.
• 3. GOS M., JABŁOŃSKI M., 1999 : Klejenie żywicą aminową ( F2 - M2 ) drewna zmodyfikowanego związkami winylowymi. Konferencja "Drewno i materiały drewnopochodne w konstrukcjach budowlanych" Szczecin - Świnoujście, 27- 28.09.1999 г., 255-259.
• 4. GOS. В., LEWANDOWSKI W. 1983 : Badanie właściwości fizykochemicznych lignomeru. Mater, na IV Symp. Nauk. „Modyfikacja drewna" PAN, AR Poznań, 181- 183.
• 5. JABŁOŃSKI M., ŚWIETLICZNY M. 1985 : Sposób otrzymywania elementów konstrukcyjnych z drewna zmodyfikowanego. Patent nr 139378.
• 6. ŁAWNICZAK M. 1976 : Sposób polimeryzacji monomerów w drewnie. Patent nr 81908.
• 7. ŚWIETLICZNY M., JABŁOŃSKI M., SEDLIAČIK J. 2003 : Applilication of Dynomel L - 435 adhesive for gluing thermally treated wood. „Pokroky vo vyrobe a použiti lepidiel v drevopriemysle" Zvolen, 3-5 września 2003 г., 186 - 190.
• 8. WÓJTOWICZ А. 1983 : Niektóre aspekty modyfikowania drewna za pomocą związków winylowych. Rozprawy Naukowe i Monografie. Wyd. SGGW-AR.

Uwagi

PL

Rekord w opracowaniu